Converting E. coli into a foundry for bioplastics

Poly(lactic acid) (PLA) is a plastic that has become very attractive as of late due to various properties that make it an excellent biomaterial. It is biodegradable, having a typical lifetime of about 6 months to 2 years until microorganisms break it down into water and carbon dioxide. It is biocompatible, degrading throughout the entire plastic instead of starting with the outermost layer, allowing the body’s immune response to break down the pieces before it has the time to overreact and damage surrounding tissues. It is bioabsorbable, allowing it to be resorbed into the body for applications such as spinal implants, slowly transferring the load to the body and allowing the bone to heal in a physically supportive environment. Lastly, it is thermoplastic, allowing it to be extruded in filament form and reshaped, as in a three-dimensional (3D) printer. Unfortunately, conventional methods of synthesizing PLA chemically are quite expensive: one gram of pure PLA costs around $90. Moreover, even though it is mostly manufactured from corn, the processing and purifying steps use many chemicals that are environmentally unfriendly.

Recently, researchers have genetically engineered E. coli to produce PLA, but at low yields and at insufficiently long chain lengths for commercial use. We propose using multiplex automated genome engineering (MAGE) to improve both the yield and chain length of biosynthesized PLA. MAGE is recombineering on steroids. MAGE takes advantage of the λ Red recombination proteins to increase the efficiency of mutation rate. Instead of laboriously targeting sites one-by-one, many areas of the genome are targeted in parallel. By repeating the procedure numerous times, an incredible amount of diversity can be created in a relatively short amount of time.

Team.jpg