Team:Imperial College/Electron microscopy

From 2013.igem.org

(Difference between revisions)
 
(13 intermediate revisions not shown)
Line 3: Line 3:
<p> A good way to observe the function of a degradation enzyme is to incubate it with the polymer and scan the surface after some time with an electron micrograph. This is a widely used method for studying plastic degradation and we are applying  it for characterising Proteinase K enzyme ([http://parts.igem.org/Part:BBa_K1149008 BBa_K1149008]) and recording how it "chews" on a PLA cup. </p>
<p> A good way to observe the function of a degradation enzyme is to incubate it with the polymer and scan the surface after some time with an electron micrograph. This is a widely used method for studying plastic degradation and we are applying  it for characterising Proteinase K enzyme ([http://parts.igem.org/Part:BBa_K1149008 BBa_K1149008]) and recording how it "chews" on a PLA cup. </p>
-
<p> PLA can spontaneously hydrolyse in water. However, this only happens very slowly and at higher temperatures. Here is a SEM image from the literature (see references). We are expecting our enzymes to have at least as visible effect in 3 or less days.</p>
+
<p> PLA can spontaneously hydrolyse in water. However, this only happens very slowly and at higher temperatures. Below  are SEM images of the process, taken from the literature (see references).</p>
https://static.igem.org/mediawiki/parts/2/2d/PLA_hydrolisis_SEM.jpg
https://static.igem.org/mediawiki/parts/2/2d/PLA_hydrolisis_SEM.jpg
<br> SEM images of the surface of PLA incubated for 9 and 20 days in deionized water at 58 °C.
<br> SEM images of the surface of PLA incubated for 9 and 20 days in deionized water at 58 °C.
-
 
+
<p>We are expecting our enzymes to have at least as visible effect in 3 or less days.</p>
<h5>method</h5>
<h5>method</h5>
We cut small pieces of the cup and washed them with ethanol and then with deionised water in order to remove any potential contamination.  
We cut small pieces of the cup and washed them with ethanol and then with deionised water in order to remove any potential contamination.  
<br>
<br>
-
https://static.igem.org/mediawiki/parts/e/e0/2013-09-27_12.47.05.jpg
 
-
<p>The samples 1A, 2A and 3A were incubated with 350 uL cell lysate of E.coli MG1655 transformed with BBa_K1149008, for 1, 2 and 3 days. </p>
+
https://static.igem.org/mediawiki/parts/7/7a/Pla_prapared_for_SEM.jpg
-
<p>Sample 1B, 2B and 3B were incubated with proteinase K enzyme solution for 1, 2 and 3 days. (** Units, lets do a LOT)</p>
+
-
<p>The negative control A was treated with cell lysate from MG1655 E.coli strain containing the empty vector and the negative control B is a PLA piece with no treatment. </p>
+
<p><b>Samples 1A, 2A and 3A </b> were incubated with 1mL proteinase K enzyme solution (purchased from Sigma Aldrich) for 1, 2 and 3 days. (0.667 mg enzyme in 1mL  PK Buffer per sample) The negative control A is PLA piece incubated with PK Buffer at 37°C, shaking. </p>
 +
<p><b>Samples 1B, 2B and 3B</b> were incubated with 1mL cell lysate-PK buffer solution (1:2) of E.coli MG1655 transformed with BBa_K1149008, for 1, 2 and 3 days. The negative control B was incubated with cell lysate solution (1:2) from MG1655 E.coli strain containing the empty vector. </p>
 +
<p><b>Sample C0</b> was not treated with anything. </p>
 +
(please see [https://2013.igem.org/Team:Imperial_College/Protocols protocols] for preparation of lysate and PK buffer)
-
All experiments were carried out at ? degrees. We have used a xxxx electron micrograph at the [http://www3.imperial.ac.uk/materials/facilities/em Harvey Flower Microstructural Characterisation Suite], Imperial College.
+
All experiments were carried out at 37 degrees, shaking in a 1.5 mL tube. (summer in greece) We have used a scanning electron micrograph at the [http://www3.imperial.ac.uk/materials/facilities/em Harvey Flower Microstructural Characterisation Suite], Imperial College.
<h5>results</h5>
<h5>results</h5>
-
Below come all the fabulous images we shall hopefully have:
 
-
https://static.igem.org/mediawiki/parts/8/83/PLA_SEM_plans.jpg
+
[[File:PLA SEM all ICL.jpg|thumbnail|center|1000px|<b>Scanning Electron Micrographs show the increased pitting of PLA surface after enzyme and cell lysate treatment. (Images by Imperial College iGEM Team 3013)</b>]]
 +
 
 +
 
 +
 
<br>
<br>

Latest revision as of 17:57, 4 October 2013

Contents

Scanning Electron Microscopy

A good way to observe the function of a degradation enzyme is to incubate it with the polymer and scan the surface after some time with an electron micrograph. This is a widely used method for studying plastic degradation and we are applying it for characterising Proteinase K enzyme ([http://parts.igem.org/Part:BBa_K1149008 BBa_K1149008]) and recording how it "chews" on a PLA cup.

PLA can spontaneously hydrolyse in water. However, this only happens very slowly and at higher temperatures. Below are SEM images of the process, taken from the literature (see references).

PLA_hydrolisis_SEM.jpg
SEM images of the surface of PLA incubated for 9 and 20 days in deionized water at 58 °C.

We are expecting our enzymes to have at least as visible effect in 3 or less days.

method

We cut small pieces of the cup and washed them with ethanol and then with deionised water in order to remove any potential contamination.

Pla_prapared_for_SEM.jpg

Samples 1A, 2A and 3A were incubated with 1mL proteinase K enzyme solution (purchased from Sigma Aldrich) for 1, 2 and 3 days. (0.667 mg enzyme in 1mL PK Buffer per sample) The negative control A is PLA piece incubated with PK Buffer at 37°C, shaking.

Samples 1B, 2B and 3B were incubated with 1mL cell lysate-PK buffer solution (1:2) of E.coli MG1655 transformed with BBa_K1149008, for 1, 2 and 3 days. The negative control B was incubated with cell lysate solution (1:2) from MG1655 E.coli strain containing the empty vector.

Sample C0 was not treated with anything.

(please see protocols for preparation of lysate and PK buffer)

All experiments were carried out at 37 degrees, shaking in a 1.5 mL tube. (summer in greece) We have used a scanning electron micrograph at the [http://www3.imperial.ac.uk/materials/facilities/em Harvey Flower Microstructural Characterisation Suite], Imperial College.

results
Scanning Electron Micrographs show the increased pitting of PLA surface after enzyme and cell lysate treatment. (Images by Imperial College iGEM Team 3013)



references

Effect of NR on the hydrolytic degradation of PLA, Huang et al., 2013